NO.: | HR316(L) | HR420 | HR430 |
Production process | Stainless Steel Powder | Stainless Steel Powder | Stainless Steel Powder |
Grade: | Atomized | Atomized | Atomized |
Density | app.4.1-4.5 tap.>4.8 g/cm3 | app.4.1-4.5 tap.>4.8 g/cm3 | app.4.1-4.5 tap.>4.8 g/cm3 |
Hardness | 36HRC | HRC50 | HRC51 |
Size | 150um | 150um | 150um |
75um | 75um | 75um | |
45um | 45um | 45um | |
15um | 15um | 15um | |
Content | Cr:16-18 Ni:10-14 Mo:2-3 C:0.08(0.03) Si:1max Mn:2max Fe:bal. | Cr:12-14 C:0.25max Si:1max Mn:1max Fe:bal. | Cr:16-18 C:0.12max Si:1max Mn:1max Fe:bal. |
Stainless Steel 316L Powder Properties | ||||||||||
Size Range | 0~25um | 0~45um | 15~45um | 45~105um | 75~180um | |||||
Morphology | Spherical | Spherical | Spherical | Spherical | Spherical | |||||
PSD | D10: 6µm | D10: 9µm | D10: 14µm | D10: 53µm | D10: 78µm | |||||
D50:16µm | D50: 25µm | D50: 35µm | D50: 69µm | D50: 120µm | ||||||
D90: 23µm | D90: 39µm | D90: 45µm | D90: 95µm | D90: 165µm | ||||||
Flow ability | N/A | ≤35S | ≤30S | ≤18S | ≤20S | |||||
Apparent Density | 3.7g/cm3 | 3.9g/cm3 | 3.9g/cm3 | 4.2g/cm3 | 4.3g/cm3 | |||||
Tap Density | 5.4g/cm3 | 5.3g/cm3 | 5.3g/cm3 | 5.3g/cm3 | 5.2g/cm3 |