产品描述
ITEM BRAND Al2O3 % ≥ RUL 0.2Mpa℃ ≥ PLC % Creep Rate % T*20-50*0.2Mpa Thermal Shock Resistance 1100 ℃ Water cool , Cycle ≥ CCS Mpa ≥ BD,g/cm ³ ≥ AP,% ≤
Hot Blast Stove Clay brick HRN42 42 1420 / 0.2 @1200℃ / 40 2 22
HRN45 45 1420 / 0.2 @1250℃ / 40 2.05 22
Low Creep Alumina Brick DRL145 65 / ±0.2 @1500*4h 0.8 @1450℃ 10 49 2.45 23
Silica Brick RGQ SiO2% ≥95 1650 Thermal Expansion % @ 1000℃ ≤ 1.26 0.8 @1500℃ Residual Quartz% ≤1.0 40 Wet 2.34 22
Andalusite Mullite Brick HLR135 53 / ±0.2 @1400*4h 0.6 @1350℃ 20 40 2.3 22
HLR145 65 / ±0.2 @1500*4h 0.6 @1450℃ 20 40 2.4 22
Clay brick HRN42 42 1420 / / 30 49 2.35 23
Silica Brick RGQ SiO2% ≥95 1650 Thermal Expansion % @ 1000℃ ≤ 1.26 0.8 @1500℃ Residual Quartz% ≤1.0 40 Wet 2.34 22
Dense Clay Brick DRN42 42 1420 / / / 40 2.15 22
Cordierite Brick JQS55 55 1450 ±0.2 @1450*2h / 80 @1200℃ 40 2.55
22