Product Introduction:
3A Molecular Sieve, is an alkali metal alumina silicate. It is the potassium form of the type A crystal structure.
It has an effective pore opening of about 3 angstroms(0.3nm). This is large enough to allow in moisture, but excludes molecules such as unsaturated hydrocarbons which can potentially form polymers.
Xintao 3A Molecular Sieve, has the advantages of faster adsorption speed, more regeneration times, higher crushing strength, stronger anti-pollution ability, greater utilization efficiency and longer service life.
Chemical Molecular Formula: 0.4K2O·0.6Na2O·Al2O3·2SiO2··4.5H2O. (SiO2 : Al2O3 ≈2).
Technical Parameter:
Model | 3A Molecular Sieve |
Color | White grey |
Nominal pore diameter | 3 angstroms |
Shape | Sphere | Pellet |
Diameter | 1.6-2.5 (mm) | 3.0-5.0 (mm) | 1.6 (mm) | 3.2 (mm) |
| 8*12 (mesh) | 4*8 (mesh) | 1/16 (inch) | 1/8 (inch) |
Bulk density (g/ml) | ≥0.72 | ≥0.72 | ≥0.68 | ≥0.68 |
Crushing strength (N/PC) | ≥40.0 | ≥85.0 | ≥30.0 | ≥70.0 |
Size ratio up to grade (%) | ≥98.0 | ≥98.0 | ≥96.0 | ≥96.0 |
Dynamic H2O adsorption (%) | ≥20.0 | ≥20.0 | ≥20.0 | ≥20.0 |
Static H2O adsorption (%) | ≥21.0 | ≥21.0 | ≥21.0 | ≥21.0 |
Static C2H4 adsorption (mg/g) | ≤3.0 | ≤3.0 | ≤3.0 | ≤3.0 |
H2O content (%) | ≤1.5 | ≤1.5 | ≤1.5 | ≤1.5 |
Wear ratio (%) | ≤0.25 | ≤0.25 | ≤0.40 | ≤0.40 |
Typical Application:
Be mainly used for the drying of petroleum cracking gas such as ethylene, propylene, butadiene
and other unsaturated hydrocarbons.
Drying of highly polar compounds, such as methanol and ethanol.
Drying of air.
Drying of natural gas and methane gas.
Warranty: By National Standard GB/T 10504-2008.
Attention: Store in a cool & dry place.