316l Stainless steel powder is widely used in powder silver sintering, pressing, metal injection molding, thermal spraying, metal shot blasting and other industries.
NO.: | 304(L) | 316(L) | 174PH |
Production Process | Atomized | Atomized | Atomized |
Grade: | 304(L) | 316(L) | 17-4PH |
Density | App.4.1-4.5 Tap.>4.9 G/cm3 | App.4.1-4.5 Tap.>4.8 G/cm3 | App.4.1-4.5 Tap.>4.8 G/cm3 |
Hardness | 34.5HRC | 36HRC | 35HRC |
Size | 150um | 150um | 150um |
75um | 75um | 75um | |
45um | 45um | 45um | |
15um | 15um | 15um | |
Content | Cr:18-20 Ni:8-12 C:0.08(0.03) Si:1max Mn:2max Fe:bal. | Cr:16-18 Ni:10-14 Mo:2-3 C:0.08(0.03) Si:1max Mn:2max Fe:bal. | Cr:15.5-17.5 Ni:3-5 Nb:0.15-0.45 Cu:3-5 C:0.07 Si:1max Mn:1max Fe:bal. |
Applications | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.6g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 | MIM part weight:0.03-200g Apparent relative density>95% Sinter density>7.8g/cm3 sinter temperature:1360-1380c Shrinkage rate:1.18 |